Basic Info.
Model NO.
20*12*159mm
Condition
New
Co
8%
Wc
92%
Hardness
89.5hra
Density
14.8g/cm3
T.R.S
2600MPa
Surface
Only Sitered
Transport Package
25kg. Carton
Specification
YG8C
Trademark
ZZUP
Origin
Zhuzhou, Hunan, China
HS Code
820900100
Production Capacity
10000000PCS/Month
Product Description
8% Co Coarse Particle 20*12*159mm for Producing Sands Tungsten Carbide block
8% Co Coarse Particle 20*12*159mm for Producing Sands Tungsten Carbide block
Specifications
8% Co Coarse Particle 20*12*159mm for Producing Sands Tungsten Carbide block
Specifications
1. YG8,YG6,YG10,YG15,YG20,YG25,YL10.2,YS2T,YG6X,YG8C ,YG10C ,YG11C etc all kinds of grades for your choose.
2. Supply sintered or ground and polished surface.
3. Can HIP sintered,higher harndess, strength and density.
4. We have more than 1000 sets molds for different sizes.
5. Supply customized package.
6. Can product customize sizes and shape.
As the core accessory of vertical impact crusher (sand making machine), the sand making machine alloy bar is widely used in mining, sand, cement, metallurgy, hydropower engineering and other industries.
Aiming at the characteristics of high-speed impact of the sand making machine stone, a specific formula and process were adopted to improve the wear resistance of the product on the premise of ensuring impact toughness.
Depending on the stone and alloy grade, the service life of each alloy can reach 40-70 hours.
It can customize the throwing heads of various brands of sand making machines, especially for river pebble, etc. The service life is greatly improved, which will greatly reduce the cost for customers.
The special hard alloy bar used in the abrasive block (throwing head) of the sand making machine is particularly suitable for sand making and ore processing.
Sand maker alloy bar performance characteristics:
1. Adapt to different material crushing requirements of users. Such as: granite, basalt, limestone, quartzite, gneiss, cement clinker, concrete aggregate, ceramic raw materials, iron ore, gold ore, copper ore, corundum, bauxite, silica, etc.
2. Compared with other materials, it has the advantages of good comprehensive performance, high reliability, strong wear resistance, and low price!
3. The length of the alloy bar can be customized according to the specifications of the throwing head, and the service life of each alloy can reach 40-70 hours.
2. Supply sintered or ground and polished surface.
3. Can HIP sintered,higher harndess, strength and density.
4. We have more than 1000 sets molds for different sizes.
5. Supply customized package.
6. Can product customize sizes and shape.
As the core accessory of vertical impact crusher (sand making machine), the sand making machine alloy bar is widely used in mining, sand, cement, metallurgy, hydropower engineering and other industries.
Aiming at the characteristics of high-speed impact of the sand making machine stone, a specific formula and process were adopted to improve the wear resistance of the product on the premise of ensuring impact toughness.
Depending on the stone and alloy grade, the service life of each alloy can reach 40-70 hours.
It can customize the throwing heads of various brands of sand making machines, especially for river pebble, etc. The service life is greatly improved, which will greatly reduce the cost for customers.
The special hard alloy bar used in the abrasive block (throwing head) of the sand making machine is particularly suitable for sand making and ore processing.
Sand maker alloy bar performance characteristics:
1. Adapt to different material crushing requirements of users. Such as: granite, basalt, limestone, quartzite, gneiss, cement clinker, concrete aggregate, ceramic raw materials, iron ore, gold ore, copper ore, corundum, bauxite, silica, etc.
2. Compared with other materials, it has the advantages of good comprehensive performance, high reliability, strong wear resistance, and low price!
3. The length of the alloy bar can be customized according to the specifications of the throwing head, and the service life of each alloy can reach 40-70 hours.
Products Show
Grades choosing
| Grade | Density g/cm3 | Hardnes HRA | T.R.S Mpa | Performance&application recommended |
| YG6C | 14.90 | 90.5 | 2400 | Good wear resistance,suitable for machining hard, rawwood,aluminum section bar,brass rod and cast iron. |
| YG6X | 14.85 | 92.5 | 2000 | Wear resistance higher than YG6,suitable for machining hard,rawwood,aluminum section bar,brass rod and cast iron. |
| YG8C | 14.7 | 89.8 | 2800 | High wear and impact resistance,suitable for machining dry wood,soft wood and non-ferrous metal section bar |
| YS2T | 14.25 | 92.0 | 2400 | Fine grain alloy,with high wear resistance,bending strength,bonding resistance and thermal strength.lt is suitable formachining refractory alloys,stainless steel,high manganesesteel,etc. |
| YL10.2 | 14.45 | 91.8 | 3000 | Wear resistance and strength comparatively higher,suitable for machining cast iron,non-ferrous metal and non-metallid materials |
Other grades and sizes can be offered as per customers' requirements
Packing details
Shipping ways
Production process
Contact details