Basic Info.
Model NO.
GM-1
Density
1.70-1.92g/cm3
Resistivity
Less Than 12
Compressive Strength
More Than 70MPa
Porosity
Less Than 26%
Elasticity Modulus
6-18gpa
Thermal Expansion Coefficient
1.47-4.25
Temperature Resistance
Less Than 4350 Degree
Ash Content
Less Than 0.05%
Property1
Low Wear/ Durable
Property2
Low Coefficient of Friction
Property3
Self-Lubricating
Property4
High Thermal Conductivity
Property5
Low Coefficient of Thermal Expansion
Property6
High Strength
Property7
Chemical Resistance
Transport Package
Cartons in Wooden Cases
Specification
personalized customized
Trademark
L. T graphite
Origin
Cn
HS Code
3801909000
Production Capacity
500000/Month
Product Description
Artificial Graphite Hot Pressing Mold Used For Pressure Sintering Of Cemented Carbide
lttrade.en.made-in-china.comA: Company profile
L.T Group has a comprehensive product and technology portfolio that focuses on four
fields of graphite - ultrafine particle graphite mould, graphite electrode, graphite crucible,
as well as other products mainly made of graphite.
Graphite materials exhibit unique properties such as good electrical and thermal
conductivity, heat and corrosion resistance, low friction, and reduced weight while at
the same time maintaining high strength. Due to the shortage of energy and raw materials,
our high performance products made from graphite are in increasingly high demand in
industries. They also play a progressively important role in everyday life, thereby
substituting traditional materials.
![Artificial Graphite Hot Pressing Mold Used for Pressure Sintering of Cemented Carbide](http://img6.grofrom.com/www.heruicarbideco.com/226f3j00lICEyskzbNgt/Artificial-Graphite-Hot-Pressing-Mold-Used-for-Pressure-Sintering-of-Cemented-Carbide.webp)
B: Product features
1. The processing materials are ultrafine granule structure, high purity and graphite
with high graphitization degree.
2. High hardness, good anti-oxidation performance and high machining accuracy
3. Good conductivity, high resistivity, sufficient mechanical strength
4. Small porosity and dense structure.
5. Excellent thermal shock resistance, conductive and thermal conductivity.
6. High temperature resistance, corrosion resistance, acid and alkali resistance,
good wear resistance.
7. Surface can be treated with anti-oxidation.
![Artificial Graphite Hot Pressing Mold Used for Pressure Sintering of Cemented Carbide](http://img6.grofrom.com/www.heruicarbideco.com/226f3j00qHMayfoKbNzE/Artificial-Graphite-Hot-Pressing-Mold-Used-for-Pressure-Sintering-of-Cemented-Carbide.webp)
C: Processing method
1. Customer provide design drawings.
2. Our technical team will check, analyze the drawings, and divide the drawing to
reasonable parts if needed, and prepare proper graphite blocks .
3. Our mechanics will design and customize grinding wheel.
4. Our workers will grinding and polishing graphite block according to the instructions
of mechanics. This process may need operating few times if needed. We will strictly keep
deviation within ±0.03-0.08mm.
5. Then our packing team will assembling different parts into a whole graphite mold.
During the assembling period, unqualified products will be picked out.
![Artificial Graphite Hot Pressing Mold Used for Pressure Sintering of Cemented Carbide](http://img6.grofrom.com/www.heruicarbideco.com/226f3j00cLvTFPbtaypQ/Artificial-Graphite-Hot-Pressing-Mold-Used-for-Pressure-Sintering-of-Cemented-Carbide.webp)
D: Attribute table
Density g/cm³ | 1.75-1.9 |
Resistivity μΩ·m | ≤18 |
Compressive strength Mpa | 40-80 |
Porosity % | ≤26 |
Elasticity Modulus Gpa | 6-18 |
Thermal expansion coefficient 10-6/ºC | 1.47-4.25 |
Ash content % | ≤0.5 |
Temperature resistance ºC | ≤4350 |
![Artificial Graphite Hot Pressing Mold Used for Pressure Sintering of Cemented Carbide](http://img6.grofrom.com/www.heruicarbideco.com/226f3j00oIMQOcqHbygT/Artificial-Graphite-Hot-Pressing-Mold-Used-for-Pressure-Sintering-of-Cemented-Carbide.webp)