Basic Info.
Model NO.
A0616M06
Application
Metal Cutting Machine
Model No.
A0616m06
Shape
Hemispherical
Applications
Hanging Mill
Flute
Double Flute
Strength
2600MPa
Hardness
89.5hra
Transport Package
Carton
Specification
17.00cm * 16.00cm * 10.00cm
Trademark
ZZUP
Origin
Zhuzhou, Hunan, China
HS Code
8209009000
Production Capacity
10000000PCS/Month
Packaging & Delivery
Package Size
17.00cm * 16.00cm * 10.00cm
Package Gross Weight
0.050kg
Product Description
Carbide Rotary Burr, also known as hard alloy high-speed assorted milling cutters, hard alloy mold milling cutters, etc., are used together with electric mills or pneumatic tools. Cemented carbide rotary files are widely used in industries such as machinery, automobiles, shipbuilding, chemical engineering, and process engraving. It can be used to process cast iron, cast steel, carbon steel, alloy steel, stainless steel, hardened steel, copper, and aluminum. Due to the manual control of cemented carbide rotary files mounted on high-speed rotating tools, the pressure and feed speed experienced by cemented carbide rotary files determine the tool's service life and cutting effect.
Main advantages of Carbide Rotary Burr:
1. Wide application range, high machining hardness. Can process cast iron, cast steel, carbon steel, alloy steel, stainless steel, copper, aluminum and other metals, and marble, jade, bone and other non-metals. The machining hardness can reach HRA ≥ 85.
2. High production efficiency and long service life. The processing efficiency is tens of times higher than that of a manual file, and nearly ten times higher than that of a small grinding wheel with a handle. Its durability is ten times higher than that of high-speed steel cutters and more than 200 times higher than that of small grinding wheels.
3. Easy to master, easy to use, safe and reliable.
4. Low carbon environmental protection, no dust pollution.
5. High processing quality and high finish.
6. The processing cost can be greatly reduced, and the comprehensive cost can be reduced by tens of times.
| Grade | Density(g/cm3) | Hardness (HRA) | T.R.S (MPa) | Grain size (μm) | Composition (%) | Equal to ISO |
| YU12 | 14.1~14.15 | .≥92.5 | ≥4000 | 0.2~0.5 | 12% CO 88% WC | K40~K50 |
| YL10.2 | 14.4~14.6 | ≥92.2 | ≥4000 | 0.6~0.8 | 10% CO 90% WC | K20~K30 |
| YG6X | 14.85~15.0 | ≥92.0 | ≥3860 | 0.8~1.0 | 6% CO 94% WC | K05 |
| YG15 | 14.0~14.1 | ≥85.0 | ≥2800 | 1.2~2.0 | 15%Co 85% WC | K30~K40 |
| YG10 | 14.5~14.6 | ≥85.5 | ≥2600 | 1.2~2.0 | 10%Co 90% WC | K20 |
| YG8 | 14.65~14.85 | ≥89.5 | ≥2320 | 1.2~2.0 | 8% CO 92% WC | K20 |
| YG6 | 14.85~15.05 | ≥90.0 | ≥2150 | 1.2~2.0 | 6% CO 94% WC | K10 |