Basic Info.
Technics
Drawing Die
Process Combination
Single-Process Mould
Manufacturing Technology
Computer Technology
Driving Motor Type
Permanent Magnet
Mold Cavity Technology
EDM Milling
Milling Speed
High Speed
Parts Detection Method
Geometric Detection
Grade
Yg15
Hardness
84.5hra
Density
14.0g/cm3
T.R.S
2800MPa
Usage
as Wear-Resistance
Transport Package
25kg. Carton
Specification
YG15C OD85*ID13.2*40 mm
Trademark
ZZUP
Origin
Zhuzhou, Hunan, China
HS Code
820900100
Production Capacity
10000000PCS/Month
Product Description
Specifications
1. Grade: YG15C , 15% Co
2. YG8,YG6,YG3,YG10,YG15,YT14,YT5,YT05,YT15,YG20,YG25,YL10.2,YS2T,YG6X etc all kinds of grades for your choose.
3. Can product customize drawing,sizes and shape.
Products Show
Grades choosing
Common grades for all kinds metal
Grades for cold mill roll or hot mill roll steel
Common grades for all kinds metal
| Grade | Density g/cm3 | Hardnes HRA | T.R.S Mpa | Performance&application recommended |
| YG6A | 14.85 | 92.5 | 2000 | Fine grain alloy,good wear resistance.it is suitable for manufacturing forming cutter,wear-resistant parts etc. |
| YG8 | 14.7 | 89.8 | 2800 | High bending strength,wear resistance lower than YG6A, suitable for manufacturing cutter ,wear-resistant parts etc. |
| YG11 | 14.4 | 88.5 | 2900 | High bending strength,wear resistance lower than YG6A, suitable for manufacturing cutter ,wear-resistant parts etc. |
| YG15 | 14.0 | 87.0 | 3000 | Suitable for manufacturing punching dies, wear-resistant parts. |
| YG20 | 13.5 | 85.5 | 2800 | High bending strength,suitable for manufacturing progressive dies and other punching dies. |
| YG25 | 13.1 | 81.5 | 2950 | High bending strength,wear resistance lower than YM6A, suitable for manufacturing cutter ,wear-resistant parts etc. |
| YS2T | 14.25 | 92.0 | 2500 | Fine grain alloy, with high wear resistance, bending strength, bonding resistance and thermal strength. it is suitable for machining refractory alloys,stainless steel, high manganese steel, etc. |
Grades for cold mill roll or hot mill roll steel
| Grade | Wc (%) | Co (%) | Ni (%) | Cr (%) | Density g/cm3 | Hardness ≥HRA | T.R.S ≥Nmm2 | Compression Strength ≥Nmm2 | Thermal Expansivity 10-6/K | Thermal Conductivity W/cm.k | Young's Elastic Modulus KN/mm2 |
| YGR60 | 70 | 30 | 12.8 | 78 | 2200 | 2900 | 7 | ||||
| YGR55 | 76 | 24 | 13.1 | 80 | 2400 | 3000 | 6.8 | 0.17 | 420 | ||
| YGR45 | 80 | 20 | 13.5 | 81 | 2500 | 3100 | 6.4 | 0.14 | 480 | ||
| YGR40 | 82 | 18 | 13.7 | 82.5 | 2600 | 3200 | 6.2 | 0.2 | 530 | ||
| YGR30 | 85 | 15 | 14.2 | 84.8 | 2700 | 3300 | 6.1 | 0.2 | 530 | ||
| YGR25 | 88 | 12 | 14.3 | 85 | 2600 | 3400 | 6 | 0.2 | 550 | ||
| YGH55 | 74 | 26 | 12.9 | 80 | 2200 | 3000 | 7 | 0.17 | 450 | ||
| YGH45 | 75 | 25 | 13.4 | 82 | 2400 | 3100 | 6.5 | 0.18 | 480 | ||
| YGH40 | 82 | 18 | 13.6 | 83.5 | 2500 | 3200 | 6.4 | 0.19 | 500 | ||
| YGH30 | 85 | 15 | 13.9 | 83.5 | 2400 | 3300 | 6.1 | 0.2 | 540 | ||
| YGH25 | 88 | 12 | 14.1 | 85 | 2300 | 3400 | 6 | 0.2 | 560 |
Common sizes:
| Outdiameter (mm) | Inner diameter (mm) | Height (mm) | Outdiameter (mm) | Inner diameter (mm) | Height (mm) | |
| 90 | 51 | 4~100 | 125 | 45 | 4~100 | |
| 90 | 20 | 125 | 80 | |||
| 90 | 3 | 130 | 40 | |||
| 95 | 75 | 130 | 50 | |||
| 95 | 68.5 | 140 | 90 | |||
| 95 | 74 | 142 | 78 | |||
| 100 | 65 | 150 | 90 | |||
| 100 | 62.1 | 210 | 200 | |||
| 100 | 20 | 161 | 108 | |||
| 105 | 46 | 212 | 120 | |||
| 105 | 65.5 | 158.8 | 87.32 | |||
| 105 | 81 | 170.66 | 95 | |||
| 105 | 75 | 180 | 87.32 | |||
| 110 | 20 | 180 | 120.65 | |||
| 110 | 30 | 228.3 | 126 | |||
| 110 | 90 | 208 | 126 | |||
| 114 | 94 | 228 | 130 | |||
| 115 | 65 | 285 | 160 | |||
| 115 | 60 | 320 | 260 | |||
| 120 | 46 | 280 | 240 | |||
| 120 | 65 | 318 | 280 | |||
| 120 | 60 | 600 | 550 | |||
| 125 | 45 | 800 | 200 |
Other sizes can be offered as per customers' requirements